In the primary ironmaking production process, the use of iron ore rich in impurities (especially phosphorus) leads to a greater difficulty during the refining of the hot metal at the Basic Oxygen Furnace. Nowadays, in the ILVA steelmaking plant of Taranto, the problems related with a high initial content of phosphorus cannot be properly faced anymore with the standard techniques. In this thesis a thermodynamic model for the dephosphoration of the hot metal into the LD converter was studied. Relying on this model, a new blowing pattern for the production of low phosphorus steel was developed. The aim was to face the issue related to a higher initial content of phosphorus and achieve lower final value compared to the standard production. The feasibility and the effectiveness of such technique were verified through a statistical analisys of the data obtained from thirtynine trial heats carried out in the ILVA steelshop number two.

Nel processo di produzione dell'acciaio tramite ciclo integrale, l'uso di minerale di ferro ricco d'impurità (come il fosforo) porta a grandi difficoltà durante l'affinazione della ghisa nei convertitori ad ossigeno. Ad oggi, nello stabilimento siderurgico ILVA di Taranto, le problematiche inerenti a elevati contenuti iniziali di fosforo non possono più essere fronteggiate con l'utilizzo di tecniche standard. In questo lavoro di tesi, è stato studiato un modello termodinamico per la defosforazione dell'acciaio all'interno dei convertitori LD. Basandosi su tale modello, si è inoltre sviluppato un nuovo pattern di soffiaggio con l'obbiettivo di fronteggiare i costanti aumenti iniziali di fosforo e cercare di raggiungere valori finali più bassi di quelli standard. L'applicabilità e l'efficienza di tale tecnica sono state verificate attraverso un'analisi statistica dei dati provenienti da trentanove colate di prova effettuate all'interno dell'acciaieria numero due di ILVA.

Model for phosphorus removal in LD converter and the design of a valuable operative practice

SOSIO, ROBERTO
2016/2017

Abstract

In the primary ironmaking production process, the use of iron ore rich in impurities (especially phosphorus) leads to a greater difficulty during the refining of the hot metal at the Basic Oxygen Furnace. Nowadays, in the ILVA steelmaking plant of Taranto, the problems related with a high initial content of phosphorus cannot be properly faced anymore with the standard techniques. In this thesis a thermodynamic model for the dephosphoration of the hot metal into the LD converter was studied. Relying on this model, a new blowing pattern for the production of low phosphorus steel was developed. The aim was to face the issue related to a higher initial content of phosphorus and achieve lower final value compared to the standard production. The feasibility and the effectiveness of such technique were verified through a statistical analisys of the data obtained from thirtynine trial heats carried out in the ILVA steelshop number two.
ING - Scuola di Ingegneria Industriale e dell'Informazione
28-apr-2017
2016/2017
Nel processo di produzione dell'acciaio tramite ciclo integrale, l'uso di minerale di ferro ricco d'impurità (come il fosforo) porta a grandi difficoltà durante l'affinazione della ghisa nei convertitori ad ossigeno. Ad oggi, nello stabilimento siderurgico ILVA di Taranto, le problematiche inerenti a elevati contenuti iniziali di fosforo non possono più essere fronteggiate con l'utilizzo di tecniche standard. In questo lavoro di tesi, è stato studiato un modello termodinamico per la defosforazione dell'acciaio all'interno dei convertitori LD. Basandosi su tale modello, si è inoltre sviluppato un nuovo pattern di soffiaggio con l'obbiettivo di fronteggiare i costanti aumenti iniziali di fosforo e cercare di raggiungere valori finali più bassi di quelli standard. L'applicabilità e l'efficienza di tale tecnica sono state verificate attraverso un'analisi statistica dei dati provenienti da trentanove colate di prova effettuate all'interno dell'acciaieria numero due di ILVA.
Tesi di laurea Magistrale
File allegati
File Dimensione Formato  
2017_04_SOSIO.pdf

non accessibile

Descrizione: Testo della tesi
Dimensione 20.67 MB
Formato Adobe PDF
20.67 MB Adobe PDF   Visualizza/Apri

I documenti in POLITesi sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10589/133808