The goal of this study is to assess the effect of both the hardening and the temperature during the operations of plastic deformation on the mechanical properties at room temperature of a manganese austenitic stainless steel. The objective consists in finding the processing parameters which allow to obtain the best mechanical performance and maintain the material amagnetic. Specimens were hot deformed to obtain different levels of strain hardening at various temperatures. It is easy with metallography to observe the hardened structure and size of the grains. Tensile tests on specimens previously hot deformed were carried out at room temperature. In this way it was possible to evaluate the mechanical properties of the material.
In questo lavoro di tesi si vuole valutare l’effetto della temperatura e del grado di incrudimento durante le operazioni di deformazione plastica sulle caratteristiche meccaniche, a temperatura ambiente, di un acciaio inossidabile austenitico al manganese. L’obiettivo del lavoro consiste nel trovare i parametri di lavorazione che consentono di ottenere le migliori prestazioni meccaniche e conservare inalterate alcune proprietà fisiche come l’amagneticità. Il materiale è stato deformato a caldo in modo da ottenere diversi gradi d’incrudimento a diverse temperature. Tramite caratterizzazione microstrutturale, prove meccaniche su provini incruditi a caldo con parametri noti è stato possibile valutare le proprietà meccaniche del materiale.
Caratterizzazione delle proprietà dell'acciaio inossidabile austenitico X10CrMnN18-18 a seguito di operazioni di forgia
CENA, CARLO VIRGILIO
2012/2013
Abstract
The goal of this study is to assess the effect of both the hardening and the temperature during the operations of plastic deformation on the mechanical properties at room temperature of a manganese austenitic stainless steel. The objective consists in finding the processing parameters which allow to obtain the best mechanical performance and maintain the material amagnetic. Specimens were hot deformed to obtain different levels of strain hardening at various temperatures. It is easy with metallography to observe the hardened structure and size of the grains. Tensile tests on specimens previously hot deformed were carried out at room temperature. In this way it was possible to evaluate the mechanical properties of the material.File | Dimensione | Formato | |
---|---|---|---|
Caratterizzazione delle proprietà dell’acciaio inossidabile austenitico X10CrMnN18-18 a seguito di operazioni di forgia.pdf
accessibile in internet solo dagli utenti autorizzati
Descrizione: Testo della tesi
Dimensione
4.39 MB
Formato
Adobe PDF
|
4.39 MB | Adobe PDF | Visualizza/Apri |
I documenti in POLITesi sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.
https://hdl.handle.net/10589/83241