Studio delle proprietà di argento a struttura ultrafine ottenuto mediante deformazione plastica severa

The mechanical properties of a metal are strongly affected by the size of its crystalline grains, which can be reduced to ultrafine and nano-sized range by severe plastic deformation. The possibility to obtain ultrafine grained metals and consequently stronger metals has attracted interest of many researchers, especially in the last decades. In spite of that, the ultrafine grained metals are still characterized by a poor ductility and an insufficient work hardening. Different solutions are still under consideration with the aim of overcoming this problem: this graduation thesis wants to study one of the mechanism of plasticity of ultrafine grained metals in depth, that is twinning deformation.

Nel campo della metallurgia è risaputo che le dimensioni dei grani cristallini influenzano sensibilmente le caratteristiche meccaniche di un metallo. La possibilità di ottenere materiali con struttura cristallina molto fine e di conseguenza con maggiore resistenza suscita da tempo particolare interesse: in questa ottica si inserisce lo studio e la produzione di metalli a grano ultrafine e nanostrutturati, in cui le dimensioni dei grani possono essere ridotte in alcuni casi fino a valori di qualche nanometro attraverso differenti tecniche. Tra i motivi che hanno finora rallentato lo sviluppo di questi materiali in forma massiva troviamo la ridotta duttilità e la scarsa capacità di incrudimento che li contraddistinguono. Sono attualmente allo studio diverse soluzioni utili per superare questo problema: per questo motivo (ma non solo) vengono studiate leghe di argento, che permettono di comprendere e approfondire uno dei meccanismi utili al raggiungimento di migliori proprietà, ovvero la deformazione per geminazione.