Surface tribological conditions play an important role in process connected with relative sliding (macroscopic or microscopic) between surfaces. From this point of view in forming process, dies and molds result strongly excited. In order to reduce wear damages and improve the surfaces properties in such kind of components a thin ceramic coating is usually applied. In this thesis the effective advantages in tribology terms of a laser surface texturing on a PVD thin ceramic coating is investigated. Conclusions arise from the results of wear, microindentation and cyclic impact tests.
Le condizioni tribologiche di una superficie svolgono un ruolo fondamentale nei processi caratterizzati da movimento relativo con connesso strisciamento, sia a livello macroscopico che microscopico. In tal senso nel processo di stampaggio i componenti di stampo e punzone risultano molto sollecitati. Al fine di ridurre i fenomeni di danneggiamento per usura è pratica diffusa migliorare le condizioni di resistenza superficiale con l’introduzione di un rivestimento dotato di elevate proprietà meccaniche. In questa tesi si andrà a verificare l’effettivo vantaggio in termini di condizioni tribologiche dell’impiego di una lavorazione di laser surface texturing a complemento di un rivestimento superficiale ceramico deposto tramite tecnica PVD. Verrà condotta un’analisi critica attraverso prove di usura, microindentazione ed impatto ciclico.
Comportamento tribologico di rivestimenti PVD in CrAlN con lavorazione di laser texturing
MUSSO, STEFANO
2015/2016
Abstract
Surface tribological conditions play an important role in process connected with relative sliding (macroscopic or microscopic) between surfaces. From this point of view in forming process, dies and molds result strongly excited. In order to reduce wear damages and improve the surfaces properties in such kind of components a thin ceramic coating is usually applied. In this thesis the effective advantages in tribology terms of a laser surface texturing on a PVD thin ceramic coating is investigated. Conclusions arise from the results of wear, microindentation and cyclic impact tests.File | Dimensione | Formato | |
---|---|---|---|
tesiLM_Musso.pdf
accessibile in internet solo dagli utenti autorizzati
Descrizione: Testo della tesi
Dimensione
10.1 MB
Formato
Adobe PDF
|
10.1 MB | Adobe PDF | Visualizza/Apri |
I documenti in POLITesi sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.
https://hdl.handle.net/10589/121536