In the present work it has been developed a proper heat treatment for the obtaining of drawn wires in Ti-6Al-4V ELI. The company Eure Inox srl, which provided the material, intends to expand the range of its production with the addition of cold drawn wire made of α-β titanium alloy of grade 23. In the production process are provided two wire drawing stages, between which is carried out a continuous heat treatment for increasing the deformability and allow further reduction of section. The purpose of this work was to determine the optimum annealing parameters. In the first place they are evaluated different heat treatments of recrystallization up to identify an acceptable time. The best thermal cycle was later adapted for the oven of the company by selecting a feed rate such to maximize the productivity without compromising the deformability. With the wire drawing of the material was confirmed that the wire annealed in this way can be plastically deformed without any breaking.
In questo elaborato è stato messo a punto un corretto trattamento termico per l’ottenimento di fili trafilati in Ti-6Al-4V ELI. L’azienda Eure Inox srl, che ha fornito il materiale, è propensa ad allargare la gamma della sua produzione con l’aggiunta di fili trafilati a freddo realizzati in lega di titanio α-β di grado 23. Nel processo di produzione sono previste due fasi di trafilatura, tra le quali viene effettuato un trattamento termico in continuo per aumentare la deformabilità e permettere un’ulteriore riduzione di sezione. Lo scopo di questo lavoro è stato quello di individuare i parametri ottimali di ricottura. Inizialmente sono stati valutati diversi trattamenti termici statici di ricristallizzazione fino ad individuare un tempo accettabile. Il ciclo termico ottimale è stato successivamente adattato per il forno dell’azienda scegliendo una velocità di avanzamento tale da massimizzare la produttività senza compromettere la deformabilità. Dalla trafilatura del materiale si ha avuto la conferma che si può deformare plasticamente il filo ricotto in tal modo senza osservare cedimenti durante questa fase.
Messa a punto di un corretto trattamento termico per l’ottenimento di fili trafilati in Ti-6Al-4V ELI
COLUZZI, DAVIDE
2015/2016
Abstract
In the present work it has been developed a proper heat treatment for the obtaining of drawn wires in Ti-6Al-4V ELI. The company Eure Inox srl, which provided the material, intends to expand the range of its production with the addition of cold drawn wire made of α-β titanium alloy of grade 23. In the production process are provided two wire drawing stages, between which is carried out a continuous heat treatment for increasing the deformability and allow further reduction of section. The purpose of this work was to determine the optimum annealing parameters. In the first place they are evaluated different heat treatments of recrystallization up to identify an acceptable time. The best thermal cycle was later adapted for the oven of the company by selecting a feed rate such to maximize the productivity without compromising the deformability. With the wire drawing of the material was confirmed that the wire annealed in this way can be plastically deformed without any breaking.File | Dimensione | Formato | |
---|---|---|---|
2016_07_Coluzzi.pdf
solo utenti autorizzati dal 07/07/2019
Descrizione: Messa a punto di un corretto trattamento termico per l’ottenimento di fili trafilati in Ti-6Al-4V ELI
Dimensione
12.45 MB
Formato
Adobe PDF
|
12.45 MB | Adobe PDF | Visualizza/Apri |
I documenti in POLITesi sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.
https://hdl.handle.net/10589/123901