Electroless deposition of NiP alloys

This thesis presents the electroless deposition of Nickel-Phosphorus (NiP) with tecnoplate3000® solutions on brass. The aim is improving and enhancing the mechanical properties of some mechanical parts. After the pretreatment of the substrate, we tried three formulations to obtain the best performance: NiP0, NiPA, NiPB; they vary mainly for the different concentration of additives. The selected one is NiPB a stable, monophase solution. At the end we added in this solution particles of carbides and ceramics to produce a hard and with high wear resistance coating. A characterization of the samples obtained was performed by optical microscope analysis, scanning electron microscope analysis (SEM), X-ray diffraction technique (XRD) and microhardness test.

In questa tesi viene presentata la deposizione electroless di Nichel-Fosforo (NiP) su ottone avvenuta grazie alla soluzione tecnoplate3000®. L’obiettivo è quello di aumentare le proprietà meccaniche e quindi le prestazioni di alcuni componenti utilizzati in meccanica. Dopo il pretrattamento del substrato, abbiamo provato tre diverse formulazioni per ottenere le migliori perfromance: NiP0, NiPA, NiPB; esse variano soprattuto per la concentrazione degli additivi. La soluzione migliore selezionata è NiPB che risulta stabile e monofasica. Alla fine in questa soluzione abbiamo aggiunto particelle di carburi e ceramici per produrre un rivestimento che fosse duro e resistente all’usura. Sono state infine effettuate prove di caratterizzazione sui provini ottenuti attraverso analisi al microscopio elettronico (SEM), diffrazione ai raggi X (XRD) e test di microdurezza.