The objective of this thesis is to study the diffusion of erucamide, an additive used to enhance the slipperiness of polyethylene films for flexible packaging. Considering the problems with the slip agent in polyethylene films, used in the production cycle, experiments have been carried out on samples of material from production, with the aim of acquire knowledge of this particular issue and improving the production of laminates. To this aim, a method of analysis has been developed in order to estimate the erucamide content in the film bulk and on the surface. This method allowed to correlate the erucamide surface content with the coefficient of friction of the polyethylene film. Further, it allowed to investigate the erucamide migration phenomenon, and to assess how surface treatments affect it. The methods and knowledge acquired were then applied to cases occurring in the industrial practice.

L'obiettivo della tesi è studiare la diffusione dell'erucamide, un additivo utilizzato per migliorare la scivolosità dei film in polietilene per imballaggi flessibili. Considerando i problemi con l’agente scivolante nei film di polietilene, utilizzati nel ciclo produttivo, sono stati svolti esperimenti su campioni di materiale da produzione, con l'obiettivo di acquisire conoscenza di questo particolare problema e migliorare la produzione di laminati. A tal fine, è stato sviluppato una procedura di analisi per stimare il contenuto di erucamide all’interno del film e sulla superficie. Questo metodo ha permesso di correlare la concentrazione superficiale dell'erucamide con il coefficiente di attrito del film di polietilene. Inoltre, ha permesso di studiare il fenomeno della migrazione dell'erucamide e di valutare come i trattamenti superficiali lo influenzano. I metodi e le conoscenze acquisite sono stati quindi applicati ai casi che si verificano nella pratica industriale.

Concentration of erucamide in polyethylene packaging : development and application of an analytical procedure in an industrial context

TESTA, ANDREA
2016/2017

Abstract

The objective of this thesis is to study the diffusion of erucamide, an additive used to enhance the slipperiness of polyethylene films for flexible packaging. Considering the problems with the slip agent in polyethylene films, used in the production cycle, experiments have been carried out on samples of material from production, with the aim of acquire knowledge of this particular issue and improving the production of laminates. To this aim, a method of analysis has been developed in order to estimate the erucamide content in the film bulk and on the surface. This method allowed to correlate the erucamide surface content with the coefficient of friction of the polyethylene film. Further, it allowed to investigate the erucamide migration phenomenon, and to assess how surface treatments affect it. The methods and knowledge acquired were then applied to cases occurring in the industrial practice.
BOSETTI, OSVALDO
ING - Scuola di Ingegneria Industriale e dell'Informazione
21-dic-2017
2016/2017
L'obiettivo della tesi è studiare la diffusione dell'erucamide, un additivo utilizzato per migliorare la scivolosità dei film in polietilene per imballaggi flessibili. Considerando i problemi con l’agente scivolante nei film di polietilene, utilizzati nel ciclo produttivo, sono stati svolti esperimenti su campioni di materiale da produzione, con l'obiettivo di acquisire conoscenza di questo particolare problema e migliorare la produzione di laminati. A tal fine, è stato sviluppato una procedura di analisi per stimare il contenuto di erucamide all’interno del film e sulla superficie. Questo metodo ha permesso di correlare la concentrazione superficiale dell'erucamide con il coefficiente di attrito del film di polietilene. Inoltre, ha permesso di studiare il fenomeno della migrazione dell'erucamide e di valutare come i trattamenti superficiali lo influenzano. I metodi e le conoscenze acquisite sono stati quindi applicati ai casi che si verificano nella pratica industriale.
Tesi di laurea Magistrale
File allegati
File Dimensione Formato  
2017_12_Testa.pdf

non accessibile

Descrizione: Testo della tesi
Dimensione 2.02 MB
Formato Adobe PDF
2.02 MB Adobe PDF   Visualizza/Apri

I documenti in POLITesi sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10589/138559