This thesis work is focused to the analysis of the mechanical characteristics and microstructures of two steel for rods, the ASTM A193-B7 and the ASTM A193-B16 to verify the fulfilling of standards of interest. For the first one the standards of reference, besides the mentioned one, are the ASTM A320-L7, UNI EN ISO 898-8.8, while for the second one is the ASTM-A193-B16. These steel are utilized to the production of bars starting from hot-rolled products as wire-rods or bars. For the evaluation of the characteristics, tensile tests, hardness tests, resilience tests, as well as an analysis of the microstructure after quenching were used.
Questo progetto di tesi si focalizza sull’analisi delle caratteristiche meccaniche e della microstruttura di due acciai da tiranteria, il ASTM A193-B7 ed il ASTM A193-B16 al fine di valutare l’ottemperanza alle normative d’interesse. Per il primo le normative di riferimento oltre la sopracitata sono l’ ASTM A 1320-L7, UNI EN ISO 898-8.8, mentre per il secondo la normative di riferimento è la ASTM A193-B16. Questi acciai vergono utilizzati per la produzione di barre a partire da laminati in forma di vergella o barre. Per l’analisi delle caratteristiche si è fatto ricorso a prove di trazione, test di durezze, test di resilienza, nonché un’ analisi della microstruttura dopo tempra.
Influence of the manufacturing cycle on mechanical properties of cold worked steels for rods
DARDANO, MICHELE
2016/2017
Abstract
This thesis work is focused to the analysis of the mechanical characteristics and microstructures of two steel for rods, the ASTM A193-B7 and the ASTM A193-B16 to verify the fulfilling of standards of interest. For the first one the standards of reference, besides the mentioned one, are the ASTM A320-L7, UNI EN ISO 898-8.8, while for the second one is the ASTM-A193-B16. These steel are utilized to the production of bars starting from hot-rolled products as wire-rods or bars. For the evaluation of the characteristics, tensile tests, hardness tests, resilience tests, as well as an analysis of the microstructure after quenching were used.File | Dimensione | Formato | |
---|---|---|---|
8-tesi intera.per caricamento-1.pdf
non accessibile
Descrizione: tesi intera
Dimensione
8.29 MB
Formato
Adobe PDF
|
8.29 MB | Adobe PDF | Visualizza/Apri |
8-tesi intera.per caricamento-2.pdf
non accessibile
Descrizione: tesi intera-2
Dimensione
8.31 MB
Formato
Adobe PDF
|
8.31 MB | Adobe PDF | Visualizza/Apri |
8-tesi intera-ultima versione.pdf
non accessibile
Dimensione
7.99 MB
Formato
Adobe PDF
|
7.99 MB | Adobe PDF | Visualizza/Apri |
I documenti in POLITesi sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.
https://hdl.handle.net/10589/138921