Optimization of the mechanical resistance of the 7050 aluminum alloy varying the aging parameters

ABSTRACT This thesis work is finalized in to find the peak hardening condition of the aluminum alloy 7050, since this alloy does not have standard T6 temper. Precipitation hardening was performed varying the aging parameters as to find at which temperature the highest hardening condition can be obtained. The aging was performed using two different ways. The first one is carried out using the dilatometer in order to reduce the investigation field. The second consist into using a traditional furnace following the aging phenomenon by performing hardness tests in prearranged time intervals. Subsequently tensile and intergranular corrosion tests were performed, at peak strength, to deeply characterize the property of the material.

SOMMARIO Questo lavoro di tesi è finalizzato nella definizione del picco di durezza della lega di alluminio 7050, dato che tale lega non ha lo stato T6 standardizzato. I trattamenti termici di solubilizzazione seguiti dall’ invecchiamento sono stati eseguiti in modo da ottenere l’indurimento da precipitazione. I parametri di invecchiamento sono stati variati in modo da identificare il picco di durezza massima. L’invecchiamento è stato eseguito in due modi differenti. Il primo è stato eseguito nel dilatometro in modo da limitare il campo d’indagine. Il secondo, utilizzando un forno tradizionale seguendo il fenomeno della precipitazione tramite prove di durezza. Successivamente sono state eseguite prove di trazione e corrosione intergranulare in modo da caratterizzare a fondo le proprietà del materiale.