Anisotropy and inhomogeneous plastic deformation in flat steel products

This study deals with the reduction and elimination of fluting lines from mild steels and boron bearing low carbon steels. The rolling process conditions including different rolling reduction, different rolling velocity ratio, and different rolling temperature were applied for mild steels to reduce fluting marks and also to obtain desirable mechanical properties. These process conditions also were used for boron bearing steels .Elimination of fluting lines from these steels were investigated. The optical and mechanical properties of the studied steels were analyzed by Optical Microscopy analysis, Transmission Electron Microscopy analysis, tensile test and bending test.

Questo studio si occupa della riduzione e dell'eliminazione delle linee di fluting da acciai dolci e da acciai a basso tenore di carbonio contenenti boro. Condizioni del processo di laminazione tra cui riduzione di laminazione, rapporto di velocità di laminazione e temperatura di laminazione sono stati cambiati per acciai dolci cercando di ridurre i segni di fluting e anche per ottenere proprietà meccaniche desiderabili. Queste condizioni di processo sono state utilizzate anche per gli acciai al boro. Inoltre, sono state studiate le linee di taglio di questi acciai. Le proprietà microstrutturale e meccaniche degli acciai studiati sono state analizzate mediante analisi al microscopio ottico, analisi di microscopia trasmissione elettronica, prove di trazione e di flessione.