For the past few decades, additive manufacturing has evolved greatly, which led to the development of 3D printing technology. 3D printing is a fast, cheap, cost effective means of production, which makes it a good fir for the construction industry. In order to reach complete automation, not enough efforts have been put into testing early strength characteristics of fresh concrete. In this thesis, a shear and a tensile test apparatus have been designed in order to suitably test concrete mixes. These tests will eventually be used to test 3D printable mixes.
Negli ultimi decenni, la produzione additiva si è evoluta notevolmente, il che ha portato allo sviluppo della tecnologia di stampa 3D. La stampa 3D è un mezzo di produzione veloce, economico ed economico, che lo rende un buon inizio per l'industria delle costruzioni. Per raggiungere l'automazione completa, non sono stati fatti sforzi sufficienti per testare le caratteristiche di resistenza precoce del calcestruzzo fresco. In questa tesi, sono stati progettati un apparato di prova di taglio e trazione per testare adeguatamente le miscele di calcestruzzo. Questi test verranno infine utilizzati per testare i mix stampabili 3D.
An experimental method to measure very early age fracture properties of HPFRCCs
EL RASSI, JOEY
2017/2018
Abstract
For the past few decades, additive manufacturing has evolved greatly, which led to the development of 3D printing technology. 3D printing is a fast, cheap, cost effective means of production, which makes it a good fir for the construction industry. In order to reach complete automation, not enough efforts have been put into testing early strength characteristics of fresh concrete. In this thesis, a shear and a tensile test apparatus have been designed in order to suitably test concrete mixes. These tests will eventually be used to test 3D printable mixes.File | Dimensione | Formato | |
---|---|---|---|
thesis final.pdf
accessibile in internet per tutti
Descrizione: Thesis text
Dimensione
8.27 MB
Formato
Adobe PDF
|
8.27 MB | Adobe PDF | Visualizza/Apri |
I documenti in POLITesi sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.
https://hdl.handle.net/10589/142712