Synthesis and hydrosolubility studies of amphiphilic core shell polymers

This paper aims at the synthesis of core-shell star polymers with hydrophilic properties (externally) and hydrophobic at the interior that can be used as polymer precursors for future catalytic applications in aqueous phase (using an appropriate functional monomers containing a coordinating function for the catalyst). This paper investigates the feasibility of such macromolecules, in this work was not made use of functional monomers. The polymers synthesized by ATRP during the experimental activity need to be soluble in water. The external chain segments were produced in poly4 vynil pirydine (quaternized) and polytbutylmethacrylate and polytbutylacrylate (hydrolyzed to give the corresponding acid soluble). The polymers obtained were characterized by GPC, HNMR, AFM and solubility tests were conducted on the final polymer obtained after the optimization of the parameters involved in the synthesis process.

Questo lavoro si propone la sintesi di polimeri a stella di tipo core-shell aventi proprietà idrofiliche (esternamente) e idrofobiche all'interno, che possano essere utilizzati come polimeri precursori per future applicazioni catalitiche in fase acquosa (mediante l'utilizzo di opportuni monomeri funzionali contenenti una funzione coordinante per il catalizzatore). In questo lavoro si indaga la fattibilità di simili macromolecole, non viene fatto impiego di monomeri funzionali. I polimeri sintetizzati mediante ATRP durante l'attività sperimentale devono essere solubili in acqua,i segmenti di catena esterni sono stati realizzati in poli4 vinipiridina (quaternizzabile), politbutilmetacrilato e politbutilacrilato (idrolizzabili per dare gli acidi idrosolubili corrispondenti).I polimeri ottenutisono stati caratteri tramite GPC, HNMR, AFM e prove di solubilità sono state condotte sui polimeri finali ottenuti, dopo l'ottimizzazione dei parametri legati al processo di sintesi.