Electrodeposition of Fe-P composite coatings with PTFE inclusions

In this thesis work Fe-P based coatings with nanometric PTFE inclusions are produced from a specific electrolyte based on iron (II) sulfate solution. During this work, the effect of the variation of the amount of PTFE in the electrolyte over the properties of the coating has been investigated. In particular, main focus is reserved to the evaluation of wettability of the coating using the contact angle on treated samples with water in order to see the effect of the increasing amount of PTFE inclusions in the bath. Subsequently, XRD and profilometry analysis have been performed.

In questo lavoro di tesi sono stati prodotti rivestimenti compositi di Fe-P con inclusioni nanometriche di PTFE a partire da una specifica soluzione elettrolitica a base di ferro solfato (II). È stato investigato l’effetto della variazione della quantità di PTFE nell’elettrolita sulle proprietà del rivestimento superficiale. Particolare attenzione è stata rivolta alla valutazione della bagnabilità del rivestimento utilizzando la tecnica dell’angolo di contatto con acqua sui campioni sottoposti a elettrodeposizione per comprendere l’effetto dell’aumento della quantità di PTFE nella soluzione. Successivamente, sono state effettuate analisi XRD e di profilometria sui campioni ottenuti.