PLA scaffolds with different porosity and surface treatments for BTE applications

Bone tissue engineering (BTE) is a field of regenerative medicine which concerned the production of implantable bone substitutes for critical bone defects that cannot heal on their own. BTE strategies combined cells, biological signals, and scaffolds, which are realized with a wide range of fabrication techniques, both traditional and additive manufacturing (AM) one. In the presented thesis work, acid polylactic (PLA) scaffolds, with different porosity and infill geometry, are realized. A mechanical and morphological characterization is performed to evaluate which, from printed scaffolds, mimic better bone tissue properties. On selected scaffolds, a biomimetic coating of biogenic apatite is performed.

Bone tissue engineering (BTE) è un ramo della medicina rigenerativa che si occupa della realizzazione di sostituti ossei a seguito di difetti critici, i quali non hanno la capacità di auto ripararsi in modo fisiologico. Le strategie per la rigenerazione del tessuto osseo combinano cellule, segnali biologici e scaffold, i quali possono essere realizzati con diverse tecniche, sia tradizionali che di additive manufacturing (AM). Nel presente lavoro di tesi, sono state realizzati scaffold di acido poli-lattico (PLA) con diverse porosità e differenti geometrie di riempimento. È stata eseguita una caratterizzazione morfologica e meccanica per valutare quali scaffold, tra quelli realizzati, mimano meglio le proprietà del tessuto osseo. Sugli scaffold selezionati, è stato realizzato un rivestimento biomimetico di apatite biogenica.