Electrodeposition of Cr-Mo alloys on steel and thermochemical treatments

The main objective of this thesis work is to develop surface properties of steel such as adhesion, hardness, Corrosion resistance, wear friction and resistance. Coating of Chromium-Molybdenum Alloys on steel can enhance these properties. Chromium based coatings are very desirable since they increase the mechanical properties of steel. Electro deposition of Cr-Mo alloys on steel through the formulated bath facilitates the deposition of alloys over a range of current density and temperature. It is also concern to keep constant pH of the electrolyte solution to maintain high deposition rate as well. The thermo chemical treatment of the deposited thin film on the steel modifies the microstructure of the surface layers by including the formation of compound layers and thick diffusion layer that improve surface topography and layer compactness.

L'obiettivo principale di questo lavoro di tesi è lo sviluppo di proprietà superficiali di acciaio come l'adesione, durezza, resistenza alla corrosione, attrito e resistenza all'usura. Un rivestimento di una lega di cromo-molibdeno sulla superficie dell’acciaio può migliorare queste proprietà. I rivestimenti a base cromo sono molto interessanti dal punto di vista applicativo in quanto migliorano le proprietà meccaniche dell'acciaio. Elettro-deposizione di leghe Cr-Mo su acciaio, utilizzando la soluzione elettrolitica scelta, facilita la deposizione di leghe su un ampio spettro di densità di corrente e temperatura. É inoltre importante mantenere costante il pH della soluzione per ottenere alti livelli di velocità di deposizione. Il trattamento termo-chimico del sottile film depositato sull'acciaio modifica la microstruttura degli strati superficiali, includendo la formazione sia di strati compositi che di spessi strati di diffusione che migliorano l’aspetto di superficie e la compattezza.