Electrodeposition of coating with MoS2 nanoparticles embedded in a Nickel metallic matrix

This study investigates the co-deposition of molybdenum disulphide nanoparticles within nickel matrix produced via electrodeposition process on carbon steel substrate. Different surfactants and their effects were investigated under three types of current: Direct current (DC), Pulse current(PC), and Pulse reverse current(PRC). To find the optimal coating, two different pH environments and three different buffers were also investigated during the experiments. The results indicate that direct current (DC) deposition at low pH and PVP-10 as surfactant, provided the highest MoS2 incorporation, particularly with maleic acid and boric acid buffers, achieving thicknesses close to 15 µm with Mo contents around 6–7%.

Questo studio analizza la co‑deposizione di nanoparticelle di disolfuro di molibdeno all’interno di una matrice di nichel ottenuta tramite processo di elettrodeposizione su un substrato in acciaio al carbonio. Sono stati esaminati diversi tensioattivi e i loro effetti sotto tre modalità di corrente: corrente continua (DC), corrente pulsata (PC) e corrente pulsata inversa (PRC). Per individuare il rivestimento ottimale, durante gli esperimenti sono stati inoltre valutati due diversi ambienti di pH e tre differenti tamponi. I risultati indicano che la deposizione in corrente continua (DC) a pH basso, utilizzando PVP‑10 come tensioattivo, ha fornito la maggiore incorporazione di MoS₂, in particolare con tamponi a base di acido maleico e acido borico, raggiungendo spessori prossimi a 15 µm con contenuti di Mo intorno al 6–7%.