Difettosità subsuperficiale di billette colate in continuo in funzione del sistema di lubrificazione

Thermical, chemical and mechanical parameters are basic in the continuous casting process in order to obtain the requested steel characteristics. If these parameters aren’t correct, the casted steel could present defects in its metallic structure, in its chemical composition and in its geometry. Other complications can be detected during the processing subsequent to the continuous casting, as the heat treatments. This work evaluates the defects detected during the process that, from the continuous casting of construction steel billets, brings to steel rods for concrete. With a systematic metallographic analysis of defected semis and finite products, the causes of the problems have been understood and improvements in order to obtain a quality product have been proposed.

Nel processo di colata continua i parametri termici, chimici e meccanici sono fondamentali per l’ottenimento di un acciaio che soddisfi i requisiti desiderati. Se questi parametri non sono corretti, l’acciaio colato può presentare difetti nella struttura metallica, nella composizione chimica e nella geometria. Ulteriori complicazioni si possono riscontrare durante le lavorazioni a valle della colata continua, come ad esempio i trattamenti termici. La tesi analizza i difetti riscontrati durante il processo produttivo che dalla colata continua di billette (di acciaio da costruzione di uso generale) porta all’ottenimento di barre di tondino ad aderenza migliorata per calcestruzzo armato. Tramite un’analisi metallografica sistematica di semilavorati e finiti difettosi, si sono comprese le cause delle anomalie di prodotto riscontrate e si sono potuti proporre interventi migliorativi atti ad ottenere un prodotto che rispetti le specifiche del caso.