Steels for aluminum die casting molds : mechanical and microstructural characterization

The thermal fatigue of steel die casting molds becomes more severe at higher operating service temperatures, reducing die life significantly. Consequently, the life of molds depends on different factors related to mechanical and microstructural properties. The aim of the present study is to characterize the mechanical and microstructural properties of some mold steels and trying to understand their effect on thermal fatigue. The experimental plan will investigate the mechanical properties from room temperature to 650 oC, whereas low cycle fatigue test will be carried out at 550 oC that is estimated from working condition. Furthermore, a microscopic analysis will be performed in order to study the non-metallic inclusion distribution and the existing microstructure.

La fatica termica degli stampi di acciaio per la pressofusione diventa più grave a temperature di esercizio più elevate, riducendo in modo significativo la vita degli stampi. Di conseguenza, essa dipende da diversi fattori legati alle proprietà meccaniche e microstrutturali. Lo scopo del presente studio è quello di caratterizzare le proprietà meccaniche e microstrutturali di alcuni stampi di acciaio e di cercare di capire il loro effetto sulla fatica termica. Il piano sperimentale studierà le proprietà meccaniche dalla temperatura ambiente a quella di 650 ° C, mentre la prova di fatica a basso ciclo sarà effettuata a 550 ° C, che è stimata come condizione di lavoro. Inoltre, un'analisi microscopica verrà effettuata con il fine di studiare la distribuzione dell'inclusione non metallica e la microstruttura esistente.