Ottimizzazione del ciclo di trattamento termico per un acciaio A707L5

A707L5 characterization was studied by mechanical tests, such as tensile, hardness and impact test, and metallographic analysis of the steel, complemented with chemical compositions and fracture’s surfaces analysis by scanning electron microscopy observation (SEM and FEG-SEM), showing changes on these properties of the steel with different heat treatments, such as quenching, annealing, ageing. It was found that information discovered were sensitive and accurate to estimate the best thermic cycle and its optimal parameters in order to obtain the best trade-off between mechanical strength and toughness . Besides, the kind of Cu precipitation behavior and perlite distribution were responsible for mechanical characteristics of the experimental steel.

La caratterizzazione dell’acciaio A707L5 è stata effettuata tramite prove meccaniche quali trazione, durezza e resilienza e analisi metallografiche, integrate con analisi delle composizioni chimiche e delle superfici di frattura mediante microscopia elettronica a scansione (SEM e FEG-SEM), mostrando modifiche sulle proprietà dell’acciaio al variare dei trattamenti termici subiti, quali tempra, rinvenimento e invecchiamento. Si è riscontrato che le informazioni ottenute sono sensibili e precise per stimare il miglior ciclo termico e i suoi parametri ottimali per ottenere il miglior compromesso tra resistenza meccanica e tenacità. Inoltre si è osservato che la tipologia di precipitazione di Cu e la distribuzione di perlite sono responsabili delle caratteristiche meccaniche dell'acciaio sperimentale in studio.