Selective laser beam melting of AlSi10Mg alloy

The aim of this thesis work is an experimental study concerning the characterization of AlSi10Mg alloy produced via additive manufacturing (AM) with the technology of powder bed laser melting. The work has been focused on the study of the laser melting process on mechanical and microstructural properties of the material produced. Experiments have been performed by using AlSi10Mg powder and Renishaw AM250 machine provided with a pulsed wave laser of ytterbium fiber. Design of experiments was implemented in order to study the effect of the main process parameters, such as power, interaction time and build plate temperature, on porosity, microstructure, calorimetric and mechanical properties.

L’obbiettivo di questa tesi è lo studio sperimentale riguardante la caratterizzazione della lega AlSi10Mg prodotta tramite Produzione Additiva attraverso la tecnologia di fusione laser su letto di polvere. Il lavoro è stato focalizzato sullo studio del processo di fusione laser sulle proprietà microstrutturali e meccaniche del materiale prodotto. Gli esperimenti sono stati eseguiti utilizzando polvere di AlSi10Mg e la macchina Renishaw AM250 fornita di un laser ad onda pulsata in fibra all’Itterbio. I progetti degli esperimenti sono stati implementati per studiare l’effetto dei parametri principali di processo, come potenza, tempo di interazione e temperatura della piastra, sulla porosità, microstruttura, e proprietà meccaniche e calorimetriche.