Numerical simulation of the fresh state behaviour of cement pastes with a Lagrangian finite element method

Describing this thesis which consist on the numerical simulation of fresh cement pastes polimers/fibres materials, such as Styrene-Butadiene Rubber (SBR) latex, Styrene-butadiene Carboxylated (XSBR) and Wollastonite. The experimental results have been developed by the laboratories of Politecnico di Milano and Laboratory LabEST, Federal University of Rio de Janeiro. The main purpose of this thesis is related to the simulation of the mentioned cement pastes where the rheological material properties such as yield stress and plastic viscosity were taken into account. The numerical simulation was focused in carrying out the mini-cone slump test in 3D and 2D, using a code based the Particle Finite Element Method which was developed by a team of the Politecnico di Milano. The comparison between numerical simulation and experimental curves are presented in this document.

Descrivendo questa tesi che consistono nella simulazione numerica di paste di cemento fresco polimeri / materiali fibre, come ad esempio stirene-butadiene in lattice di gomma (SBR), stirene-butadiene carbossilato (XSBR) e Wollastonite. I risultati sperimentali sono stati sviluppati dai laboratori del Politecnico di Milano e Laboratorio LabEST, Università Federale di Rio de Janeiro. Lo scopo principale di questa tesi è legato alla simulazione delle paste di cemento menzionati in cui sono state prese in considerazione le proprietà del materiale reologiche quali la tensione di snervamento e la viscosità plastica. La simulazione numerica è stata focalizzata nella realizzazione del test di crollo mini-cono in 3D e 2D, utilizzando un codice basato Particle metodo degli elementi finiti che è stato sviluppato da un team del Politecnico di Milano. Il confronto tra simulazione numerica e curve sperimentali sono presentati in questo documento.